Product Details:
| Minimum Order Quantity | 50 Kg |
| Material | STAINLESS STEEL RODS |
| Finish | BRIGHT POLISH |
| Shape | ROUND |
| Size | 4 MM TO 200 |
| Color | BRIGHT |
| Usage/Application | PNEUMATICS |
| Brand | LAXCON / JINDAL / VIRAJ |
| Grade | SS 304, SS 304L. SS 316 , SS 316L |
| Country of Origin | Made in India |
Additional Information:
Product Details:
| Minimum Order Quantity | 10 Kg |
| Material Grade | 304,304L,316,316L |
| Brand | UNIFLEX |
| Usage/Application | Manufacturing |
| Single Piece Length | 3 meter |
| Test Certificate | ISO |
Additional Information:
Product Details:
| Thickness | 4.0 mm - 100 mm |
| Standard | 304 / 1.4301 |
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276, ASME SA276 |
| Finish | Bright, Black, Polish, Export Bright |
| Type | Bar, Bright Bar, Black Bars, Hex Bar |
| Length | Random, Fix & Cut Length |
| Standard | SS 304 |
| UNS | S30400 |
| WERKSTOFF NR. | 1.4301 |
| AFNOR | Z7CN18-09 |
| JIS | SUS 304 |
| GOST | 08X18H10 |
| BS | 304S31 |
| EN | X5CrNi18-10 |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 304 | 515 | 205 | 40 | 92 | 201 |
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of thermal Expansion (m/m/0C) | thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
| 0-1000C | 0-3150C | 0-5380C | at 1000C | at 5000C | |||||
| 304 | 8000 | 193 | 17.2 | 17.8 | 18.4 | 16.2 | 21.5 | 500 | 720 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 304 | min. | – | – | – | – | – | 18 | – | 8 | – |
| max. | 0.08 | 2 | 0.75 | 0.045 | 0.03 | 20 | – | 10.5 | 0.1 | |
Product Details:
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276, ASME SA276 |
| Finish | Bright, Black, Polish, Export Bright |
| Type | Bar, Bright Bar, Black Bars, Hex Bar |
| Length | Random, Fix & Cut Length |
| Standard | SS 304H |
| UNS | S30409 |
| JIS | SUS 304H |
| GOST | 08X18H10 |
| BS | 304S31 |
| EN | X5CrNi18-10 |
| BS | 304S31 |
| EN | X5CrNi18-10 |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 304 H | 515 | 205 | 40 | 92 | 201 |
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of thermal Expansion (m/m/0C) | thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
| 0-1000C | 0-3150C | 0-5380C | at 1000C | at 5000C | |||||
| 304 H | 8000 | 193 | 17.2 | 17.8 | 18.4 | 16.2 | 21.5 | 500 | 720 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 304 H | min. | 0.04 | – | – | 0.045 | – | 18 | – | 8 | – |
| max. | 0.1 | 2 | 0.75 | 0.045 | 0.03 | 20 | – | 10.5 | – | |
Product Details:
| Standard | 304L / 1.4306 |
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276, ASME SA276 |
| Finish | Bright, Black, Polish, Export Bright |
| Thickness | 4.0 mm - 100 mm |
| Standard | SS 304L |
| UNS | S30403 |
| WERKSTOFF NR. | 1.4306/1.4307 |
| AFNOR | Z3CN18-10 |
| JIS | SUS 304L |
| GOST | 03X18H11 |
| BS | 304S11 |
| EN | X2CrNi18-9 / X2CrNi19-11 |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 304 L | 485 | 170 | 40 | 92 | 201 |
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of thermal Expansion (m/m/0C) | thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
| 0-1000C | 0-3150C | 0-5380C | at 1000C | at 5000C | |||||
| 304 L | 8000 | 193 | 17.2 | 17.8 | 18.4 | 16.2 | 21.5 | 500 | 720 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 304 L | min. | - | - | – | - | – | 18 | – | 8 | – |
| max. | 0.03 | 2 | 0.75 | 0.045 | 0.03 | 20 | – | 12 | 0.1 | |
Product Details:
| Standard | 310 (1.4840 ) |
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276, ASME SA276 |
| Finish | Bright, Black, Polish, Export Bright |
| Length | Random, Fix & Cut Length |
| Standard | SS 310 |
| UNS | S31000 |
| WERKSTOFF NR. | 1.484 |
| JIS | SUS 310 |
| BS | 310S21 |
| EN | X8CrNi25-21 |
| BS | 304S11 |
| EN | X2CrNi18-9 / X2CrNi19-11 |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 310 | 515 | 205 | 40 | 95 | 217 |
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of thermal Expansion (m/m/0C) | thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
| 0-1000C | 0-3150C | 0-5380C | at 1000C | at 5000C | |||||
| 310 | 7750 | 200 | 15.9 | 16.2 | 17 | 14.2 | 18.7 | 500 | 720 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 310 | min. | - | - | – | - | – | 24 | – | 19 | – |
| max. | 0.25 | 2 | 1.5 | 0.045 | 0.03 | 26 | – | 22 | – | |
Product Details:
| Standard | 310H |
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276, ASME SA276 |
| Finish | Bright, Black, Polish, Export Bright |
| Thickness | 4.0 mm - 100 mm |
| Standard | SS 310H |
| UNS | S31009 |
| JIS | 310H |
| BS | 31009 |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 310 H | 515 | 205 | 40 | 95 | 217 |
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of thermal Expansion (m/m/0C) | thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
| 0-1000C | 0-3150C | 0-5380C | at 1000C | at 5000C | |||||
| 310 H | 7750 | 200 | 15.9 | 16.2 | 17 | 14.2 | 18.7 | 500 | 720 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 310 H | min. | - | - | – | - | – | 24 | – | 19 | – |
| max. | 0.25 | 2 | 1.5 | 0.045 | 0.03 | 26 | – | 22 | – | |
Product Details:
| Standard | 304 / 1.4301 |
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276,ASME SA276 |
| Finish | Bright,Black,Polish,Export Bright |
| Thickness | 4.0 mm - 100 mm |
| Length | Random,Fix & Cut Length |
| Standard | SS 304 |
| UNS | S30400 |
| WERKSTOFF NR. | 1.4301 |
| AFNOR | Z7CN18-09 |
| JIS | SUS 304 |
| GOST | 08X18H10 |
| BS | 304S31 |
| EN | X5CrNi18-10 |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 304 | 515 | 205 | 40 | 92 | 201 |
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of thermal Expansion (m/m/0C) | thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
| 0-1000C | 0-3150C | 0-5380C | at 1000C | at 5000C | |||||
| 304 | 8000 | 193 | 17.2 | 17.8 | 18.4 | 16.2 | 21.5 | 500 | 720 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 304 | min. | – | – | – | – | – | 18 | – | 8 | – |
| max. | 0.08 | 2 | 0.75 | 0.045 | 0.03 | 20 | – | 10.5 | 0.1 | |
Product Details:
| Standard | AISI304H (S30409) |
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276, ASME SA276 |
| Finish | Bright, Black, Polish, Export Bright |
| Thickness | 4.0 mm - 100 mm |
| Standard | SS 304H |
| UNS | S30409 |
| JIS | SUS 304H |
| GOST | 08X18H10 |
| BS | 304S31 |
| EN | X5CrNi18-10 |
| BS | 304S31 |
| EN | X5CrNi18-10 |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 304 H | 515 | 205 | 40 | 92 | 201 |
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of thermal Expansion (m/m/0C) | thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
| 0-1000C | 0-3150C | 0-5380C | at 1000C | at 5000C | |||||
| 304 H | 8000 | 193 | 17.2 | 17.8 | 18.4 | 16.2 | 21.5 | 500 | 720 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 304 H | min. | 0.04 | – | – | 0.045 | – | 18 | – | 8 | – |
| max. | 0.1 | 2 | 0.75 | 0.045 | 0.03 | 20 | – | 10.5 | – | |
Product Details:
| Standard | 304L / 1.4306 |
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276, ASME SA276 |
| Finish | Bright, Black, Polish, Export Bright |
| Type | Bar, Bright Bar, Black Bars, Hex Bar, Square Bar |
| Length | Random, Fix & Cut Length |
| Standard | SS 304L |
| UNS | S30403 |
| WERKSTOFF NR. | 1.4306/1.4307 |
| AFNOR | Z3CN18-10 |
| JIS | SUS 304L |
| GOST | 03X18H11 |
| BS | 304S11 |
| EN | X2CrNi18-9 / X2CrNi19-11 |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 304 L | 485 | 170 | 40 | 92 | 201 |
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of thermal Expansion (m/m/0C) | thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
| 0-1000C | 0-3150C | 0-5380C | at 1000C | at 5000C | |||||
| 304 L | 8000 | 193 | 17.2 | 17.8 | 18.4 | 16.2 | 21.5 | 500 | 720 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 304 L | min. | - | - | – | - | – | 18 | – | 8 | – |
| max. | 0.03 | 2 | 0.75 | 0.045 | 0.03 | 20 | – | 12 | 0.1 | |
Product Details:
| Type | Bar, Bright Bar, Black Bars, Hex Bar, Square Bar |
| Standard | 310S / 1.4845 |
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276, ASME SA276 |
| Length | Random, Fix & Cut Length |
| Standard | SS 310S |
| UNS | S31008 |
| WERKSTOFF NR. | 1.4845 |
| AFNOR | X12CrNi2521 |
| JIS | 310S |
| EN | X12CrNi2521 |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 310 S | 515 | 205 | 40 | 95 | 217 |
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of thermal Expansion (m/m/0C) | thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
| 0-1000C | 0-3150C | 0-5380C | at 1000C | at 5000C | |||||
| 310 S | 8000 | 193 | 17.2 | 17.8 | 18.4 | 16.2 | 21.5 | 500 | 720 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 310 S | min. | - | - | – | - | – | 24 | – | 19 | – |
| max. | 0.25 | 2 | 1.5 | 0.045 | 0.03 | 26 | – | 22 | – | |
Product Details:
| Standard | 316Ti / 1.4571 |
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276, ASME SA276 |
| Finish | Bright, Black, Polish, Export Bright |
| Length | Random, Fix & Cut Length |
| Standard | SS 316Ti |
| UNS | S31635 |
| WERKSTOFF NR. | 1.4571 |
| AFNOR | Z6CNDT17‐12 |
| JIS | SUS 316Ti |
| GOST | 08Ch17N13M2T |
| BS | 320S31 |
| EN | X6CrNiMoTi17-12-2 |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 316 TI | 500-700 | 200 | 40 | 95 | 215 |
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of thermal Expansion (m/m/0C) | thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
| 0-1000C | 0-3150C | 0-5380C | at 1000C | at 5000C | |||||
| 316 TI | 8000 | 193 | 15.9 | 16.2 | 17.5 | 16.3 | 21.5 | 500 | 740 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 316 TI | min. | - | - | – | - | – | 16.5 | 2 | 10.5 | – |
| max. | 0.08 | 2 | 0.75 | 0.045 | 0.03 | 18.5 | 3 | 13.5 | 0.1 | |
Product Details:
| Standard | 316L / 1.4404 |
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276, ASME SA276 |
| Finish | Bright, Black, Polish, Export Bright |
| Thickness | 4.0 mm - 100 mm |
| Standard | SS 316L |
| UNS | S31603 |
| WERKSTOFF NR. | 1.4404 |
| AFNOR | Z3CND17‐11‐02 |
| JIS | SUS 316L |
| GOST | 03Ch17N14M3 |
| BS | 316S11 |
| EN | X2CrNiMo17-12-2 |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 316 L | 485 | 170 | 40 | 95 | 217 |
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of thermal Expansion (m/m/0C) | thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
| 0-1000C | 0-3150C | 0-5380C | at 1000C | at 5000C | |||||
| 316 L | 8000 | 193 | 15.9 | 16.2 | 17.5 | 16.3 | 21.5 | 500 | 740 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 316 L | min. | - | - | – | - | – | 16 | 2 | 10 | – |
| max. | 0.08 | 2 | 0.75 | 0.045 | 0.03 | 18 | 3 | 14 | 0.1 | |
Product Details:
| Minimum Order Quantity | 10 Kg |
| Shape | Square |
| Usage/Application | Industrial |
| Size | >40 mm |
| Brand | UNIFLEX |
| Standard | 316L / 1.4404 |
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276,ASME SA276 |
| Length | Random,Fix & Cut Length |
| Standard | SS 316L |
| UNS | S31603 |
| WERKSTOFF NR. | 1.4404 |
| AFNOR | Z3CND17???11???02 |
| JIS | SUS 316L |
| GOST | 03Ch17N14M3 |
| BS | 316S11 |
| EN | X2CrNiMo17-12-2 |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 316 L | 485 | 170 | 40 | 95 | 217 |
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of thermal Expansion (m/m/0C) | thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
| 0-1000C | 0-3150C | 0-5380C | at 1000C | at 5000C | |||||
| 316 L | 8000 | 193 | 15.9 | 16.2 | 17.5 | 16.3 | 21.5 | 500 | 740 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 316 L | min. | - | - | – | - | – | 16 | 2 | 10 | – |
| max. | 0.08 | 2 | 0.75 | 0.045 | 0.03 | 18 | 3 | 14 | 0.1 | |
Product Details:
| Standard | 316H |
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276, ASME SA276 |
| Finish | Bright, Black, Polish, Export Bright |
| Thickness | 4.0 mm - 100 mm |
| Standard | SS 316H |
| UNS | 31609 |
| JIS | SUS 316H |
| BS | 316S09 |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 316 H | 515 | 205 | 40 | 95 | 217 |
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of thermal Expansion (m/m/0C) | thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
| 0-1000C | 0-3150C | 0-5380C | at 1000C | at 5000C | |||||
| 316 H | 8000 | 193 | 15.9 | 16.2 | 17.5 | 16.3 | 21.5 | 500 | 740 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 316 H | min. | 0.04 | - | – | - | – | 16 | 2 | 10 | – |
| max. | 0.1 | 2 | 0.75 | 0.045 | 0.03 | 18 | 3 | 14 | 0.1 | |
Product Details:
| Standard | 321H / 1.4878 |
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276, ASME SA276 |
| Finish | Bright, Black, Polish, Export Bright |
| Thickness | 4.0 mm 100 mm |
| Standard | SS 321H |
| UNS | S32109 |
| WERKSTOFF NR. | 1.4878 |
| JIS | SUS 321H |
| BS | 321S51 |
| EN | X10CrNiTi18-10 |
| Density | 7.92 g/cm³ |
| Melting Point | 1398-1446° C |
| Tensile Strength | Psi – 75000 , MPa – 515 |
| Yield Strength (0.2%Offset) | Psi – 30000 , MPa – 205 |
| Elongation | 45 % |
| Grade | Density (g/m3) | Elastic Modulus (GPa) | Thermal Conductivity (W/m.K) | Electrical Resistivity (μohm/cm) |
| 321H | 7.92/td> | 193 | 14.6 | 7.4 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | Other |
| 321H | -0.08 | 2 | 0.75 | 0.045 | 0.03 | 17.019.0 | – | 9.012.0 | 0.1 | Ti=5(C+N)0.70 |
Product Details:
| Standard | 347 / 1.4550 |
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276, ASME SA276 |
| Thickness | 4.0 mm - 100 mm |
| Length | Random, Fix & Cut Length |
| Standard | SS 347 |
| UNS | S3470 |
| WERKSTOFF NR. | 1.455 |
| JIS | SUS 347 |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 347 | 515 | 205 | 40 | 92 | 217 |
| Grade | Density (g/m3) | Elastic Modulus (GPa) | Thermal Conductivity (W/m.K) | Electrical Resistivity (μohm/cm) |
| 347 | 7.93 | 190-210 | 16-18 @ 20-100 | 70-73 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Other | |
| 347 | min. | - | - | – | - | – | 17 | - | 9 | Nb=10(C+N) |
| max. | 0.1 | 2 | 0.75 | 0.045 | 0.03 | 18 | 3 | 14 | 0.1 | |
Product Details:
| Standard | 347H / 1.4961 |
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276, ASME SA276 |
| Finish | Bright, Black, Polish, Export Bright |
| Thickness | 4.0 mm - 100 mm |
| Length | Random, Fix & Cut Length |
| Standard | SS 347H |
| UNS | S34709 |
| JIS | SUS 347H |
| BS | S34709 |
| WERKST.OFF | 1.4961 |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 347 H | 515 | 205 | 35 | 95 | 217 |
| Density lbm/in3 | Coefficient of Thermal Expansion (min/in)-°F | Thermal Conductivity BTU/hr-ft-°F | Specific Heat BTU/lbm -°F | Modules of Elasticity (annealed)2-psi | |
| at 68 °F | at 68 – 212°F | at 68 – 1832°F | 68-932°F | at 32 – 212°F | in tension (E) |
| 0.288 | 9.2 | 11.4 | 14.7 | 0.12 | 28 x 106 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 347 H | min. | 0.04 | - | – | - | – | 17 | 3 | 9 | |
| max. | 0.1 | 2 | 0.75 | 0.045 | 0.03 | 19 | 4 | 13 | 0.1 | |
Product Details:
| Standard | 347H / 1.4961 |
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276, ASME SA276 |
| Thickness | 4.0 mm - 100 mm |
| Length | Random, Fix & Cut Length |
| Standard | SS 347H |
| UNS | S34709 |
| JIS | SUS 347H |
| BS | S34709 |
| WERKST.OFF | 1.4961 |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 347 H | 515 | 205 | 35 | 95 | 217 |
| Density lbm/in3 | Coefficient of Thermal Expansion (min/in)-°F | Thermal Conductivity BTU/hr-ft-°F | Specific Heat BTU/lbm -°F | Modules of Elasticity (annealed)2-psi | |
| at 68 °F | at 68 – 212°F | at 68 – 1832°F | 68-932°F | at 32 – 212°F | in tension (E) |
| 0.288 | 9.2 | 11.4 | 14.7 | 0.12 | 28 x 106 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 347 H | min. | 0.04 | - | – | - | – | 17 | 3 | 9 | |
| max. | 0.1 | 2 | 0.75 | 0.045 | 0.03 | 19 | 4 | 13 | 0.1 | |
Product Details:
| Minimum Order Quantity | 10 Kilogram |
| Finish | Bright, Black, Polish, Export Bright |
| Standard | 904L / 1.4539 |
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276, ASME SA276 |
| Thickness | 4.0 mm - 100 mm |
| Length | Random, Fix & Cut Length |
| Type | Bar, Bright Bar, Black Bars, Hex Bar, Square Bar, Rods |
| Standard | SS 904L |
| UNS | N08904 |
| WERKSTOFF NR. | 1.4539 |
| JIS | SUS 904L |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 904 L | 490 | 220 | 35 | 70-90 typical | – |
| Rockwell Hardness value range is typical only; other values are specified limit | |||||
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of thermal Expansion (m/m/0C) | thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
| 0-1000C | 0-3150C | 0-5380C | at 1000C | at 5000C | |||||
| 904 L | 8000 | 200 | 15 | - | - | 13 | - | 500 | 850 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Cu | |
| 904 L | min. | - | - | – | - | – | 19 | 4 | 23 | 1 |
| max. | 0.2 | 0.2 | 1 | 0.045 | 0.035 | 23 | 5 | 28 | 2 | |
Product Details:
| Standard | 310S / 1.4845 |
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276,ASME SA276 |
| Finish | Bright,Black,Polish,Export Bright |
| Thickness | 4.0 mm - 100 mm |
| Standard | SS 310S |
| UNS | S31008 |
| WERKSTOFF NR. | 1.4845 |
| AFNOR | X12CrNi2521 |
| JIS | 310S |
| EN | X12CrNi2521 |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 310 S | 515 | 205 | 40 | 95 | 217 |
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of thermal Expansion (m/m/0C) | thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
| 0-1000C | 0-3150C | 0-5380C | at 1000C | at 5000C | |||||
| 310 S | 8000 | 193 | 17.2 | 17.8 | 18.4 | 16.2 | 21.5 | 500 | 720 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 310 S | min. | - | - | – | - | – | 24 | – | 19 | – |
| max. | 0.25 | 2 | 1.5 | 0.045 | 0.03 | 26 | – | 22 | – | |
Product Details:
| Minimum Order Quantity | 10 Kilogram |
| Type | Bar, Bright Bar, Black Bars, Hex Bar, Square Bar |
| Standard | 321 / 1.4541 |
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276, ASME SA276 |
| Finish | Bright, Black, Polish, Export Bright |
| Standard | SS 321 |
| UNS | S32100 |
| WERKSTOFF NR. | 1.4541 |
| JIS | SS 321 |
| BS | 321S00 |
| Density | 7.92 g/cm³ |
| Melting Point | 1398-1446° C |
| Tensile Strength | Psi – 75000 , MPa – 515 |
| Yield Strength (0.2%Offset) | Psi – 30000 , MPa – 205 |
| Elongation | 45 % |
| Grade | Density (g/cm3) | Elastic Modulus (GPa) | Thermal Conductivity (W/m.K) | Electrical Resistivity (μohm/cm) |
| 321 | 7.92 | 193 | 14.6 | 7.4 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | Other |
| 321 | -0.08 | 2 | 0.75 | 0.045 | 0.03 | 17.019.0 | – | 9.012.0 | 0.1 | Ti=5(C+N)0.70 |
Product Details:
| Minimum Order Quantity | 10 Kg |
| Shape | Hexagonal |
| Usage/Application | Manufacturing |
| Type | hex |
| Material | Stainless Steel |
| Surface Finish | Aluminium Finish |
| Application | Construction |
| Unit Length | 3 - 6 Mtr |
| Technique | Hot Rolled |
| Color | Metallic Grey |
| Payment Terms | Immediate |
| Test Certificate | 3.1 |
| Size | 3 mm - 400 mm |
| Dimensions | 5.5 mm - 500 mm |
Product Details:
| Minimum Order Quantity | 10 Kg |
| Material Grade | 904L |
| Size | 16 TO 130 MM |
| Shape | Round |
| Usage/Application | Manufacturing |
| Brand | UNIFLEX |
| Single Piece Length | 6 meter, 0.5 - 3 METER, 3 meter |
| Test Certificate | 3.1 |
| Thickness/Diameter | 2-3 inch, 0-1 inch, 1-2 inch |
| Finish | Polished |
| Product Type | BRIGHT POLISH |
| Thickness/Diameter | 0-1 inch,1-2 inch,2-3 inch,3-4 inch,>4 inch |
| Brand | UNIFLEX |
| Application | Manufacturing,Construction |
| Single Piece Length | 18 meter,36 meter,>36 meter,3 meter,6 meter |
Round Bars made of 904L Stainless Steel are carefully outlined and engineered using high quality metals that are highly demanded because of its unwavering quality and strength. The mentioned product is an ideal choice to be used in the corrosive environments for rendering outstanding resistance against pitting, crevice, stress, inter-granular corrosion. Moreover, Stainless Steel Round Bars provide better weld-ability and form-ability in comparison to the conventional grades. It is capable of withstanding temperature up to 450 degree Celsius. Our offered 904L Bars have high tensile and yield strength that make them a perfect solution for fulfilling different requirements.
Applications:
Additional Information:
Product Details:
| Material Grade | SS 304 / 316L |
| Shape | Round |
| Usage/Application | Industrial |
| Size | 10 DIA-130 |
| Brand | VIRAJ / JSL |
| Type | BLACK BRIGHT |
| Material | Stainless Steel |
| Single Piece Length | 6 meter |
| Thickness/Diameter | >4 inch |
Product Details:
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276, ASME SA276 |
| Finish | Bright, Black, Polish, Export Bright |
| Thickness | 4.0 mm - 100 mm |
| Standard | SS 310 |
| UNS | S31000 |
| WERKSTOFF NR. | 1.484 |
| JIS | SUS 310 |
| BS | 310S21 |
| EN | X8CrNi25-21 |
| BS | 304S11 |
| EN | X2CrNi18-9 / X2CrNi19-11 |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 310 | 515 | 205 | 40 | 95 | 217 |
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of thermal Expansion (m/m/0C) | thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
| 0-1000C | 0-3150C | 0-5380C | at 1000C | at 5000C | |||||
| 310 | 7750 | 200 | 15.9 | 16.2 | 17 | 14.2 | 18.7 | 500 | 720 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 310 | min. | - | - | – | - | – | 24 | – | 19 | – |
| max. | 0.25 | 2 | 1.5 | 0.045 | 0.03 | 26 | – | 22 | – | |
Product Details:
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276, ASME SA276 |
| Finish | Bright, Black, Polish, Export Bright |
| Type | Hex Bar, Square Bar, Rods, Polish Bar |
| Standard | SS 310H |
| UNS | S31009 |
| JIS | 310H |
| BS | 31009 |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 310 H | 515 | 205 | 40 | 95 | 217 |
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of thermal Expansion (m/m/0C) | thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
| 0-1000C | 0-3150C | 0-5380C | at 1000C | at 5000C | |||||
| 310 H | 7750 | 200 | 15.9 | 16.2 | 17 | 14.2 | 18.7 | 500 | 720 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 310 H | min. | - | - | – | - | – | 24 | – | 19 | – |
| max. | 0.25 | 2 | 1.5 | 0.045 | 0.03 | 26 | – | 22 | – | |
Product Details:
| Standard | 316 / 1.4401 |
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276, ASME SA276 |
| Thickness | 4.0 mm - 100 mm |
| Standard | SS 316 |
| UNS | S31600 |
| WERKSTOFF NR. | 1.4401 |
| AFNOR | Z7CND17‐11‐02 |
| JIS | SS 316 |
| BS | 316S31 |
| EN | X5CrNiMo17-12-2 |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 316 | 515 | 205 | 40 | 95 | 217 |
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of thermal Expansion (m/m/0C) | thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
| 0-1000C | 0-3150C | 0-5380C | at 1000C | at 5000C | |||||
| 316 | 7750 | 200 | 15.9 | 16.2 | 17 | 14.2 | 18.7 | 500 | 720 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 316 | min. | - | - | – | - | – | 16 | 2 | 10 | – |
| max. | 0.08 | 2 | 0.75 | 0.045 | 0.03 | 18 | 3 | 14 | 0.1 | |
Product Details:
| Standard | 316 / 1.4401 |
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276, ASME SA276 |
| Length | Random, Fix & Cut Length |
| Standard | SS 316 |
| UNS | S31600 |
| WERKSTOFF NR. | 1.4401 |
| AFNOR | Z7CND17‐11‐02 |
| JIS | SS 316 |
| BS | 316S31 |
| EN | X5CrNiMo17-12-2 |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 316 | 515 | 205 | 40 | 95 | 217 |
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of thermal Expansion (m/m/0C) | thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
| 0-1000C | 0-3150C | 0-5380C | at 1000C | at 5000C | |||||
| 316 | 7750 | 200 | 15.9 | 16.2 | 17 | 14.2 | 18.7 | 500 | 720 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 316 | min. | - | - | – | - | – | 16 | 2 | 10 | – |
| max. | 0.08 | 2 | 0.75 | 0.045 | 0.03 | 18 | 3 | 14 | 0.1 | |
Product Details:
| Standard | 321H / 1.4878 |
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276, ASME SA276 |
| Type | Bar, Bright Bar, Black Bars, Hex Bar, Square Bar |
| Standard | SS 321H |
| UNS | S32109 |
| WERKSTOFF NR. | 1.4878 |
| JIS | SUS 321H |
| BS | 321S51 |
| EN | X10CrNiTi18-10 |
| Density | 7.92 g/cm³ |
| Melting Point | 1398-1446° C |
| Tensile Strength | Psi – 75000 , MPa – 515 |
| Yield Strength (0.2%Offset) | Psi – 30000 , MPa – 205 |
| Elongation | 45 % |
| Grade | Density (g/m3) | Elastic Modulus (GPa) | Thermal Conductivity (W/m.K) | Electrical Resistivity (μohm/cm) |
| 321H | 7.92/td> | 193 | 14.6 | 7.4 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | Other |
| 321H | -0.08 | 2 | 0.75 | 0.045 | 0.03 | 17.019.0 | – | 9.012.0 | 0.1 | Ti=5(C+N)0.70 |
Product Details:
| Type | Bar, Bright Bar, Black Bars, Hex Bar |
| Standard | 347 / 1.4550 |
| Range | 3.17 mm to 350 mm dia |
| Finish | Bright, Black, Polish, Export Bright |
| Standard | SS 347 |
| UNS | S3470 |
| WERKSTOFF NR. | 1.455 |
| JIS | SUS 347 |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 347 | 515 | 205 | 40 | 92 | 217 |
| Grade | Density (g/m3) | Elastic Modulus (GPa) | Thermal Conductivity (W/m.K) | Electrical Resistivity (μohm/cm) |
| 347 | 7.93 | 190-210 | 16-18 @ 20-100 | 70-73 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Other | |
| 347 | min. | - | - | – | - | – | 17 | - | 9 | Nb=10(C+N) |
| max. | 0.1 | 2 | 0.75 | 0.045 | 0.03 | 18 | 3 | 14 | 0.1 | |
Product Details:
| Minimum Order Quantity | 10 Kilogram |
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276, ASME SA276 |
| Finish | Bright, Black, Polish, Export Bright |
| Thickness | 4.0 mm - 100 mm |
| Standard | SS 904L |
| UNS | N08904 |
| WERKSTOFF NR. | 1.4539 |
| JIS | SUS 904L |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 904 L | 490 | 220 | 35 | 70-90 typical | – |
| Rockwell Hardness value range is typical only; other values are specified limit | |||||
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of thermal Expansion (m/m/0C) | thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
| 0-1000C | 0-3150C | 0-5380C | at 1000C | at 5000C | |||||
| 904 L | 8000 | 200 | 15 | - | - | 13 | - | 500 | 850 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Cu | |
| 904 L | min. | - | - | – | - | – | 19 | 4 | 23 | 1 |
| max. | 0.2 | 0.2 | 1 | 0.045 | 0.035 | 23 | 5 | 28 | 2 | |
Product Details:
| Finish | Bright, Black, Polish, Export Bright |
| Standard | 321 / 1.4541 |
| Range | 3.17 mm to 350 mm dia |
| Designation | ASTM A276, ASME SA276 |
| Thickness | 4.0 mm - 100 mm |
| Standard | SS 321 |
| UNS | S32100 |
| WERKSTOFF NR. | 1.4541 |
| JIS | SS 321 |
| BS | 321S00 |
| Density | 7.92 g/cm³ |
| Melting Point | 1398-1446° C |
| Tensile Strength | Psi – 75000 , MPa – 515 |
| Yield Strength (0.2%Offset) | Psi – 30000 , MPa – 205 |
| Elongation | 45 % |
| Grade | Density (g/cm3) | Elastic Modulus (GPa) | Thermal Conductivity (W/m.K) | Electrical Resistivity (μohm/cm) |
| 321 | 7.92 | 193 | 14.6 | 7.4 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | Other |
| 321 | -0.08 | 2 | 0.75 | 0.045 | 0.03 | 17.019.0 | – | 9.012.0 | 0.1 | Ti=5(C+N)0.70 |
Product Details:
| Minimum Order Quantity | 15 Kg |
| Shape | Square |
| Usage/Application | Manufacturing |
| Size | >40 mm |
| Type | square & hex |
| Material | Stainless Steel |
| Surface Finish | Black & Bright |
| Material Grade | 304, 304L, 316 , 316L |
| Single Piece Length | 6 meter, 3 meter |
Additional Information:
Product Details:
| Minimum Order Quantity | 50 Kg |
| Shape | C Channel |
| Material Grade | SS 304 & SS 316 |
| Usage/Application | Automobile Industry |
| Channel Type | C CHANNEL,H CHANNEL,I CHANNEL |
| Application | Oil & Gas Industry, Construction, Automobile Industry, Pharmaceutical / Chemical Industry |
| Material | Stainless Steel |
| Type | C Channel |
Our clients can avail an extensive range of Stainless Steel Channels, which are highly demanded by our clients for quick performance, user friendly and eco-friendly features. Our products can be bent according to the desired configuration. These products are specially outsourced from the top manufacturers, and they are known for high quality, durability and resistant to corrosion. These are offered to the customers at legal prices.
Specifications:
Standard:
S.S.304 Channel
S.S.304L Channel
S.S.316 Channel
S.S.316L Channel
S.S.316Ti Channel
S.S.321 Channel
S.S.347 Channel
S.S.309 Channel
S.S.310 Channel
S.S.310S Channel
S.S.409 Channel
S.S.409M Channel
S.S.410 Channel
S.S.410S Channel
S.S.420 Channel
S.S.430 Channel
S.S.440C Channel
Additional Information:
4.8/5
Reviewed by 17 Users
Most Relevant Reviews