Product Details:
Steel Grade | AISI316 (1.4401) |
Production | Hot-Rolled |
Standard | ASTM A240/A480 |
Thickness | 3.0 mm-30.0 mm |
Width | 1000 mm, 1250 mm, 1500 mm, 2000 mm |
Package Weight | 1.0-4.0 ton |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
316 | min. max. | – 0.08 | – 2.0 | – 0.75 | – 0.045 | – 0.030 | 16.0 18.0 | 2.00 3.00 | 10.0 14.0 | – 0.10 |
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
316 | 515 | 205 | 40 | 95 | 217 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (μm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100°C (J/kg.K) | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
316 | 8000 | 193 | 15.9 | 16.2 | 17.5 | 16.3 | 21.5 | 500 | 740 |
Product Details:
Minimum Order Quantity | 50 Kg |
Material Grade | SS316L |
Brand | UNIFLEX INDIA |
Shape | Round |
Unit Pipe Length | 6 meter |
Material | Stainless Steel |
Thickness | 0.5-60 mm |
Finish | Matt Bright |
Size | 1/2 inch, 3/4 inch, 1 inch, 2 inch |
Length | 3m, 6m, 12m, or As Per Requirement |
Unit Pipe Length | 3 meter, 6 meter, 9 meter, 18 meter, Customized |
Features | Anealed, Pickled, Polished, Cold Drawn |
Packaging Type | Shrink Wrapping, Jute Wrapping, Bubble Wrapping, Wooden Boxes or As Per Requirement |
Is It Rust Proof | Rust Proof |
Is It Corrosion Resistant | Corrosion Resistant |
I Deal In | New Only |
Minimum Order Quantity | 500 Kilogram |
Additional Information:
Product Details:
Steel Grade | AISI316H |
Width | 1000 mm,1250 mm,1500 mm,2000 mm |
Production | Hot-Rolled |
Standard | ASTM A240/A480 |
Thickness | 3.0 mm-30.0 mm |
Package Weight | 1.0-4.0 ton |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
316 H | min. max. | 0.04 0.10 | – 2.0 | – 0.75 | – 0.045 | – 0.03 | 16.0 18.0 | 2.00 3.00 | 10.0 14.0 | – 0.10 |
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
316 H | 515 | 205 | 40 | 95 | 217 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (μm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100°C (J/kg.K) | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
316 H | 8000 | 193 | 15.9 | 16.2 | 17.5 | 16.3 | 21.5 | 500 | 740 |
Product Details:
Steel Grade | AISI316TI (1.4571) |
Production | Hot-Rolled |
Standard | ASTM A240/A480 |
Thickness | 3.0 mm-30.0 mm |
Width | 1000 mm, 1250 mm, 1500 mm, 2000 mm |
Package Weight | 1.0-4.0 ton |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
316 TI | min. max. | – 0.08 | – 2.0 | – 0.75 | – 0.045 | – 0.03 | 16.50 18.50 | 2.00 3.00 | 10.50 13.50 | – 0.10 |
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
316 TI | 500-700 | 200 | 40 | 95 | 215 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (μm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100°C (J/kg.K) | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
316 TI | 8000 | 193 | 15.9 | 16.2 | 17.5 | 16.3 | 21.5 | 500 | 740 |
Product Details:
Steel Grade | AISI310H |
Production | Hot-Rolled |
Standard | ASTM A240/A480 |
Thickness | 3.0 mm-30.0 mm |
Width | 1000 mm, 1250 mm, 1500 mm, 2000 mm |
Package Weight | 1.0-4.0 ton |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
310 H | min. max. | – 0.25 | – 2.0 | – 1.50 | – 0.045 | – 0.030 | 24.0 26.0 | – | 19.0 22.0 | – |
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
310 H | 515 | 205 | 40 | 95 | 217 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (μm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100°C (J/kg.K) | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
310 H | 7750 | 200 | 15.9 | 16.2 | 17 | 14.2 | 18.7 | 500 | 720 |
Grade | UNS No | Old British | Euronorm | Swedish SS | Japanese JIS | ||
BS | En | No | Name | ||||
310 H | S310H00 | 310H24 | – | 1.484 | X15CrNi25-20 | – | SUH 310H |
Product Details:
Steel Grade | AISI347/ (1.4550) |
Production | Hot-Rolled |
Standard | ASTM A240/A480 |
Thickness | 3.0 mm-30.0 mm |
Width | 1000 mm, 1250 mm, 1500 mm, 2000 mm |
Package Weight | 1.0-4.0 ton |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Other | |
347 | min. max. | – 0.08 | – 2.0 | – 1.00 | – 0.045 | – 0.03 | 17.0 20.0 | – | 9.00 13.00 | Nb=10(C+N) 1.0 |
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
347 | 515 | 205 | 40 | 92 | 201 |
Thermal Expansion | 16-18 @ 20-100 | °C |
Melting Point | 1400-1425 | °C |
Modulus Elasticity | 190-210 | GPa |
Electrical Resistivity | 70-73 | μohm/cm |
Density | 7.93 | g/cm3 |
Grade | UNS No | Old British | Euronorm | Swedish SS | Japanese JIS | ||
BS | En | No | Name | ||||
347 | S31000 | 31024 | - | 1.484 | X15CrNi25-20 | - | SUH 310 |
Product Details:
Steel Grade | AISI321 (1.4541) |
Production | Hot-Rolled |
Standard | ASTM A240/A480 |
Thickness | 3.0 mm-30.0 mm |
Width | 1000 mm, 1250 mm, 1500 mm, 2000 mm |
Package Weight | 1.0-4.0 ton |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | Other | |
321 | min. max. | – 0.08 | – 2.0 | – 0.75 | – 0.045 | – 0.03 | – 17.019.0 | – | 9.012.0 | – 0.10 | Ti=5(C+N)0.70 |
Density | 7.92 g/cm³ |
Melting Point | 1398-1446° C |
Tensile Strength | Psi – 75000 , MPa – 515 |
Yield Strength (0.2%Offset) | Psi – 30000 , MPa – 205 |
Elongation | 45 % |
Thermal Conductivity | 14.6 | W.m -1.°K-1 |
Specific gravity | 7.92 | |
Modulus Elasticity | 193 | GPa |
Electrical Resistivity | 7.4 | μohm/cm |
Density | 7.92 | g/cm3 |
Grade | UNS No | Old British | Euronorm | Swedish SS | Japanese JIS | ||
BS | En | No | Name | ||||
321 | S32100 | 321S31 | 58B, 58C | 1.4541 | X6CrNiTi18-10 | 2337 | SUH 321 |
Product Details:
Production | Cold-Rolled |
Standard | ASTM A240/A480 |
Thickness | Min: 0.4 mm Max: 6.0 mm |
Width | 1000 mm, 1250 mm, 1500 mm, 2000 mm |
Coating | PVC coating normal/laser |
Steel Grade | AISI310S (1.4845) |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
310 S | min. max. | – 0.25 | – 2.0 | – 1.50 | – 0.045 | – 0.030 | 24.0 26.0 | – | 19.0 22.0 | – |
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
310 S | 515 | 205 | 40 | 95 | 217 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (μm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100°C (J/kg.K) | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
310 S | 8000 | 193 | 17.2 | 17.8 | 18.4 | 16.2 | 21.5 | 500 | 720 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (μm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100°C (J/kg.K) | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
310 S | 7750 | 200 | 15.9 | 16.2 | 17 | 14.2 | 18.7 | 500 | 720 |
Product Details:
Minimum Order Quantity | 50 Kilogram |
Production | Hot-Rolled |
Standard | ASTM A240/A480 |
Thickness | 3.0 mm-30.0 mm |
Width | 1000 mm, 1250 mm, 1500 mm, 2000 mm |
Steel Grade | AISI304L(1.4307) |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
304 L | min. max. | – 0.030 | – 2.0 | – 0.75 | – 0.045 | – 0.030 | 18.0 20.0 | – | 8.0 10.5 | – 0.10 |
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
304 L | 485 | 170 | 40 | 92 | 201 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (μm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100°C (J/kg.K) | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
304 L | 8000 | 193 | 17.2 | 17.8 | 18.4 | 16.2 | 21.5 | 500 | 720 |
Grade | UNS No | Old British | Euronorm | Swedish SS | Japanese JIS | ||
BS | En | No | Name | ||||
304 L | S30403 | 304S11 | – | 1.4306 | X2CrNi19-11 | 2352 | SUS 304L |
Product Details:
Thickness | 3.0 mm-30.0 mm |
Production | Hot-Rolled |
Standard | ASTM A240/A480 |
Width | 1000 mm, 1250 mm, 1500 mm, 2000 mm |
Package Weight | 1.0-4.0 ton |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
304 H | min. max. | 0.04 0.10 | – 2.0 | – 0.75 | 0.045 | – 0.030 | 18.0 20.0 | – | 8.0 10.5 | – |
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
304 H | 515 | 205 | 40 | 92 | 201 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (μm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100°C (J/kg.K) | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
304 H | 8000 | 193 | 17.2 | 17.8 | 18.4 | 16.2 | 21.5 | 500 | 720 |
Grade | UNS No | Old British | Euronorm | Swedish SS | Japanese JIS | ||
BS | En | No | Name | ||||
304 H | S30409 | 304S51 | – | 1.4948 | X6CrNi18-11 | – | – |
Product Details:
Width | 1000 mm, 1250 mm, 1500 mm, 2000 mm |
Production | Hot-Rolled |
Standard | ASTM A240/A480 |
Thickness | 3.0 mm-30.0 mm |
Steel Grade | AISI347H / (1.4961) |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
347 H | min. max. | 0.04 0.10 | – 2.0 | – 0.75 | – 0.045 | – 0.03 | 17.0 19.0 | 3.00 4.00 | 9.0 13.0 | – 0.10 |
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
347 H | 515 | 205 | 35 | 95 | 217 |
Density lbm/in3 | Coefficient of Thermal Expansion (min/in)-°F | Thermal Conductivity BTU/hr-ft-°F | Specific Heat BTU/lbm -°F | Modules of Elasticity (annealed)2-psi | |
at 68 °F | at 68 – 212°F | at 68 – 1832°F | 68-932°F | at 32 – 212°F | in tension (E) |
0.288 | 9.2 | 11.4 | 14.7 | 0.12 | 28 x 106 |
Product Details:
Production | Cold-Rolled |
Standard | ASTM A240/A480 |
Thickness | Min: 0.4 mm Max: 6.0 mm |
Coating | PVC coating normal/laser |
Steel Grade | AISI310 (1.4840 ) |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
310 | min. max. | – 0.25 | – 2.0 | – 1.50 | – 0.045 | – 0.030 | 24.0 26.0 | – | 19.0 22.0 | – |
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
310 | 515 | 205 | 40 | 95 | 217 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (μm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100°C (J/kg.K) | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
310 | 7750 | 200 | 15.9 | 16.2 | 17 | 14.2 | 18.7 | 500 | 720 |
Grade | UNS No | Old British | Euronorm | Swedish SS | Japanese JIS | ||
BS | En | No | Name | ||||
310 | S31000 | 31024 | – | 1.484 | X15CrNi25-20 | – | SUH 310 |
Product Details:
Minimum Order Quantity | 50 Kg |
Steel Grade | AISI304(1.4301) |
Production | Hot-Rolled |
Standard | ASTM A240/A480 |
Thickness | 3.0 mm-30.0 mm |
Width | 1000 mm,1250 mm,1500 mm,2000 mm |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
304 | min. max. | – 0.08 | – 2.0 | – 0.75 | – 0.045 | – 0.030 | 18.0 20.0 | – | 8.0 10.5 | – 0.10 |
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
304 | 515 | 205 | 40 | 92 | 201 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (μm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100°C (J/kg.K) | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
304 | 8000 | 193 | 17.2 | 17.8 | 18.4 | 16.2 | 21.5 | 500 | 720 |
Grade | UNS No | Old British | Euronorm | Swedish SS | Japanese JIS | ||
BS | En | No | Name | ||||
304 | S30400 | 304S31 | 58E | 1.4301 | X5CrNi18-10 | 2332 | SUS 304 |
Product Details:
Production | Hot-Rolled |
Standard | ASTM A240/A480 |
Thickness | 3.0 mm-30.0 mm |
Width | 1000 mm, 1250 mm, 1500 mm, 2000 mm |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | Other | |
321 H | min. max. | – 0.08 | – 2.0 | – 0.75 | – 0.045 | – 0.03 | – 17.019.0 | – | 9.012.0 | – 0.10 | Ti=5(C+N)0.70 |
Density | 7.92 g/cm³ |
Melting Point | 1398-1446° C |
Tensile Strength | Psi – 75000 , MPa – 515 |
Yield Strength (0.2%Offset) | Psi – 30000 , MPa – 205 |
Elongation | 45 % |
Thermal Conductivity | 14.6 | W.m -1.°K-1 |
Specific gravity | 7.92 | |
Modulus Elasticity | 193 | GPa |
Electrical Resistivity | 7.4 | μohm/cm |
Density | 7.92 | g/cm3 |
Grade | UNS No | Old British | Euronorm | Swedish SS | Japanese JIS | ||
BS | En | No | Name | ||||
321 H | S32109 | 321S51 | - | 1.4878 | X10CrNiTi18-10 | - | SUS 321H |
Product Details:
Production | Cold-Rolled |
Thickness | Min: 0.4 mm Max: 6.0 mm |
Width | 1000 mm, 1250 mm, 1500 mm, 2000 mm |
Steel Grade | AISI316L (1.4404) |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
316 L | min. max. | – 0.08 | – 2.0 | – 0.75 | – 0.045 | – 0.030 | 16.0 18.0 | 2.00 3.00 | 10.0 14.0 | – 0.10 |
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
316 L | 485 | 170 | 40 | 95 | 217 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (μm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100°C (J/kg.K) | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
316 L | 8000 | 193 | 15.9 | 16.2 | 17.5 | 16.3 | 21.5 | 500 | 740 |
Product Details:
Steel Grade | AISI904L (1.4539) |
Production | Hot-Rolled |
Standard | ASTM A240/A480 |
Thickness | 3.0 mm-30.0 mm |
Width | 1000 mm, 1250 mm, 1500 mm, 2000 mm |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
904 L | min. max. | 0.20 | – 2.0 | – 1.00 | – 0.045 | – 0.035 | 19.0 23.0 | 4.00 5.00 | 23.00 28.00 | 1.00 2.00 |
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
904L | 490 | 220 | 35 | 70-90 typical | – |
Rockwell Hardness value range is typical only; other values are specified limits. |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (μm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100°C (J/kg.K) | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
904 L | 8000 | 200 | 15 | - | - | 13 | - | 500 | 850 |